Metal-surface stainless steel spray
Metallic surface stainless steel spray
SSTSPR-400ML
Register now and access more than 60,000 products
- Excellent corrosion protection thanks to stainless steel pigment and corrosion inhibitor
- Tough elastic coating
- High resistance to external influences
- Very good adhesion to all metallic surfaces
- Spot weldable
- Fast drying
Optimum processing temperature of +20°C. Use a primer to pre-treat PU and MS sealing compounds.
See https://www.bmk.gv.at/themen/klima_umwelt/chemiepolitik/recht/eu_vo/ausgangsstoffe-explosiv.html
Datasheets(X)
For repair of stainless steel surfaces. Suitable for pipes, wrought iron, car and cargo parts. Safe to use on wood and the most common plastics.
Shake can vigorously for approx. 1 minute before use. The surface must be clean, dry and free from rust and grease. Spray the first layer thinly to create better adhesion. Observe the flash-off times between spray actions (matt surface).
Chemical basis | Acrylic resin |
Contents | 400 ml |
Colour | Steel grey |
Dry layer thickness (first back-and-forth motion) | 40 µm |
Min. dust-drying time | 20 min |
Conditions for dust-drying time | at 20°C |
Min. curing time | 4 h |
Max. curing time | 6 h |
Fully hardening/curing conditions | 20°C |
Max. temperature resistance | 200 °C |
Density | 1.06 g/cm³ |
Coating thickness | 40 µm |
Recoatable/Can be painted over | Yes, after 4-6 hours |
Shelf life from production | 24 Month |
Conditions to maintain shelf life from production | at 15°C to 25°C |
Min. flashing point | 21 °C |
Min. grip strength | 10 min |
Grip strength conditions | at 20°C |
Cross-cut test | MAN 0-1 |
Cross-cut test conditions | in accordance with DIN 53151 |
AOX-free | Yes |
Spot weldable | Yes |
Substrates with good adhesion | Wood, Metal, Cardboard, Plastic |